DUWAI DWSM-6X - Heavy Wall High Shrink Ratio Heat Shrink Tubing
APPLICATIONS
With a high shrink ratio up to 6:1, it is suitable for the insulation protection of the products with irregular shapes and large differences in outer diameter between the cables, connectors and components. The hot melt adhesive that coated inside of the tubing providing reliable and waterproof performance. It is widely used in waterproof protection for outlet hole of the fiber optic splice closures as well as optical fibers.
OPERATING TEMPERATURE RANGE
- Continuous operating temperature: -55℃ ~ 110℃
- Minimum shrink temperature: 80℃
- Full recovery temperature: Above 120˚C
COLOR
Standard color: black
- 6:1 high shrink ratio
- Waterproof, UV resistant
- Tough, abrasion resistant
6x thick-walled heat shrinkable tubing with glue is specially designed for cables, connectors, and electronic components with special inner diameters. It has high insulation and excellent mechanical protection properties. Its high shrinkage ratio of 6 times makes it widely used in products of various special sizes. 6 times thicker-walled heat shrink tubing with glue provides excellent mechanical protection for cable connectors and terminals, is impact-resistant, wear-resistant, and meets environmental protection requirements. 6x thick-walled heat shrinkable tubing with glue has UV resistance, high insulation and excellent mechanical protection properties. Its high shrinkage ratio enables it to be widely used in various special situations. Heat shrink tubing is specially designed for cables, connectors, and electronic components with special inner diameters. 6 times thicker wall heat shrinkable tube with glue is suitable for medium and low voltage insulation, wear resistance, impact resistance, sealing function, waterproof and moisture-proof.
|
Technical Data |
|
|
|
Property |
Test Method |
Typical Value |
|
Tensile strength |
ASTM D2671 |
≥12MPa |
|
Tensile strength after aging |
ASTM D2671 |
≥12MPa |
|
Elongation at break |
ASTM D2671 |
≥350% |
|
Elongation at break after aging |
ASTM D2671 |
≥300% |
|
Dielectric strength |
ASTM D2671 |
≥10kV/mm |
|
Volume resistivity |
ASTM D2671 |
≥1012Ω‧cm |
|
Heat shock |
ASTM D2671 |
No cracking |
|
Hot melt adhesive |
||
|
Softening point |
ASTM E28 |
85±5°C |
|
Water absorption |
ISO 62 |
≤0.2% |
|
Peel strength (PE) |
DIN 30672 |
≥4N/cm |